Effect of Ytterbium Nanosandwiching on The Physical Prosperities CdS thin films رسالة ماجستير

Abstract

In this study, the effects of the sandwiching of a 70 nm thick ytterbium film between two layers of CdS on the structural, compositional, optical and electrical properties are investigated. The X-ray diffraction, scanning electron microscopy, energy dispersion X-ray, visible light spectroscopy and electrical-temperature techniques are employed to achieve these effects. It was observed that, the nanosandwiching of Yb between two 500 nm thick films of CdS enhances the crystalline nature of the films without altering the lattice parameters. Particularly, the grain size is increased by 25%, the strain, the defect density and the stacking faults are reduced by 31.5%, 43.7% and 25%, respectively. Optically, the Yb nanosandwiching is observed to enhance the visible light absorbability by at least 2.7 times of the whole range and by 8 times at 1.64 eV. The enhancement of the absorbability is associated with shrinking in the band gap and more interband states. In addition, an increase in the real part of the dielectric constant by 54% is observed when Yb was nanosandwiched in the CdS structure. The modeling of the imaginary part allowed exploring the electron-plasmon interaction parameters. A remarkable increase in the drift mobility from 281 to 996 cm2/Vs associated with plasmon frequency enhancement from 0.84 to 1.38 GHz was determined upon Yb nanosandwiching.